Kinkou-XCVI aeris alleo (cu-9ni-6sn c72700)
I. Chemical Compositionem C72700
| Exemplar | Ni | Sn | Mn | Pb | Zn | Fe | P | Sordes | Cu |
| C72700 | 8.5-9.5 | 5.5-6.5 | 0.05-0.3 | ≤0.03 | ≤0.15 | ≤0.05 | ≤0.05 | ≤0.5 | Reliquus |
II. Physica proprietatibus C72700
| Densitas | 8,9 | (G / cm3) |
| Point liquescens | 968-1078 | (℃) |
| Thermal expansion coefficient | 17.25 | (X10-6/ ℃) 20-200 ℃ |
| Elastica modulus | CXX | (GPA) |
| Electrica resistentibus ad XX ℃ |
| ΜΩ * cm |
| Extinguo | ≤19.5 |
|
| DECURPATOR | ≤15 |
|
| Conductors Electrical (iacs,%) |
| (% Iacs) |
| ≥9 |
| |
| Praecipitatio duritia (III horas) | ≥12 |
|
| Torsional modulus | 50 | (GPA) |
| Ad XX ℃ scelerisque conductivity | 53.6 | (W / MK) |
| Flectentes labore vires | CDL | (MPa) |
III. Mechanica proprietatibus / rei publicae C72700
I) advolvit products
| Res | Durities | Tensile vires | CEDITAS | Elongaion | Bending * | Durness, Elasticitas et Flectens Landue Properties (MPA) | ||
| HV | RM (MPA) | R. 0.2 (MPa) | A50mm (%) | Longitudinal // | Transverso⊥ | Longitudinal // | Transverso⊥ | |
| Extemprectus | ||||||||
| TB | 90-125 | 420-500 | ≥200 | ≥30 | 0,2 | 0,2 | CCCII | CCXX |
| Quenching / frigus Rolling | ||||||||
| TD1 | 140-180 | 460-560 | ≥300 | ≥15 | 0,2 | 0,2 | CCXVI | CCCLIX |
| TD2 | 160-200 | 540-640 | ≥400 | ≥c10 | 0,2 | 0,2 | CCLXXV | CCCXC |
| TD3 | 200-240 | 620-720 | ≥55050 | ≥3 | 0,5 | 0,5 | CDXLIV | DXXIII |
| TD4 | 220-260 | 700-820 | ≥600 | ≈1 | 2 | 1 | CDLXVII | DLXVIII |
| Tdx | ≤320 | ≥780 | ≥650 | ≈1 | 10 | 2 | CDLXXII | DCXIII |
| Quenching / praecipitatio calor curatio | ||||||||
| TF | 230-270 | 740-860 | ≥510 | ≥c10 | 0,5 | 0,5 | DLXVI | DCXXXIV |
| Quenching / frigus volvens / praecipitatio calor curatio | ||||||||
| Th1 | 270-310 | 850-950 | ≥650 | ≥8 | 0,5 | 0,5 | DCLXXXIV | DCCIV |
| Th2 | 290-320 | 880-980 | ≥720 | ≥8 | 1 | 1 | DCCXXX | DCCLXX |
| Th3 | 310-340 | 950-1050 | ≥800 | ≥4 | 1 | 1 | DCCCXXIX | ≥840 |
| Th4 | 320-360 | 1000-1100 | ≥900 | ≈3 | 2 | 2 | ≥830 | ≥840 |
| Thx | ≤390 | ≥ib50 | ≥950 | ≈1 | / | / | ≥830 | ≥840 |
| *: Secundum ad Laudate V (V) XI (25/10/85), XC ° per volvens directionem, dividant minimum radius per crassitiem determinare R / T Ratio | ||||||||
II) products
| Res | Durities | Tensile vires | CEDITAS | Elongaion | Expansion coefficientem |
| HV | RM (MPA) | R. 0.2 (MPa) | A50mm (%) | Z% | |
| Extemprectus | |||||
| TB | ≤150 | 400-500 | ≥200 | ≥30 | ≥80 |
| Quenching / frigus Rolling | |||||
| TD1 | 150-180 | 500-580 | ≥300 | ≥c10 | ≥75 |
| TD2 | 180-230 | 550-720 | ≥500 | ≥3 | ≥70 |
| TD3 | 220-260 | 700-800 | ≥600 | ≥2 | ≥65 |
| TD4 | 230-300 | 780-880 | ≥700 | ≥1.5 | ≥60 |
| Tdx | 250-320 | 880-1000 | ≥800 | ≥0.1 | ≥50 |
|
|
|
|
|
|
|
| Res | HV | RM (MPA) | R. 0.2 (MPa) | A50mm (%) | Z% |
| Quenching / praecipitatio calor curatio | |||||
| TF | ≤260 | 770-870 | ≥500 | ≥20 | ≥40 |
| Quenching / frigus volvens / praecipitatio calor curatio | |||||
| Th1 | 260-300 | 870-970 | ≥700 | ≥13 | ≥30 |
| Th2 | 290-310 | 930-1030 | ≥800 | ≥8 | ≥30 |
| Th3 | 310-330 | 1000-1100 | ≥900 | ≥5 | ≥30 |
| Th4 | 330-360 | 1100-1200 | ≥1000 | ≥2 | ≥30 |
| Thx | ≥350 | 1175-1300 | ≥1100 | ≥0.5 | ≥30 |
IV. Vexillum tolerantia de virga et filum de C72700
| Genus | Diameter | Diameter tolerantia | Tolerantia rectitudo | |||
| inch | mm | inch | mm | inch | mm | |
| Filum | 0.2-0.39 | 6.35-9.9 | +/- 0.002 | +/- 0.05 | longitudo = 10ft, deviationem <0.25 pollices | longitudo = 3048mm, deviationem <6.35mm |
| 0.4-0.74 | 10-18.9 | + 0.005 / -0 | + 0,13 / -0 | |||
| Virga | 0.75-1.6 | 19-40.9 | + 0,02 / + 0,08 | + 0,5 / + 2.0 | longitudinem = 10ft, deviationem <0.5 pollices | longitudo = 3048mm, deviationem <12mm |
| 1.61-2.75 | 41-70 | + 0,02 / + 0,10 | + 0,02 / + 0,10 | |||
| 2.76-3.25 | 70.1-82 | + 0,02 / + 0,145 | + 0,02 / + 0,145 | |||
| 3.26-6.00 | 83-152.4 | + 0,02 / + 0.187 | + 0,02 / + 0.187 | |||
| <0,4 | <X | +/- 0.002 | +/- 0.05 |
|
| |
V. Application of C72700
Substitutis beryllium aeris mixturae
Est usus ad specula, electricians, electromechanical, electronics, iungo, automobiles, familia appliances, spectade industria, conversus partes